Topas Advanced Polymers TOPAS® 8007F-400 Cyclic Olefin Copolymer (COC)

Topas Advanced Polymers TOPAS® 8007F-400 Cyclic Olefin Copolymer (COC)

2019-05-28 17:09:57

  

Categories:  Polymer; Thermoplastic; Cyclo Olefin Polymer
 
Material Notes:  TOPAS® 8007F-400 is a robust film extrusion grade designed for blending with polyethylene (PE). It is a moderate clarity amorphous resin with high stiffness, moisture barrier, chemical resistance, thermoformability and purity for food and general purpose applications. It is used in blends in both cast and blown processes, and in monolayer and multilayer products. Leading film applications include twist wrap, forming webs, protective packaging, shrink films and labels, and easy tear packaging. Industrial uses include thermoforming enhancement for PE and PP sheet products.
Key applications and attributes:

•Forming films (header bags, etc.): Clarity, forming, barrier, purity, halogen-free
•Protective packaging: Stiffness for downgauging, improved forming
•Shrink films and labels: High shrink, low stress, gloss, toughness
•Twist films: Outstanding deadfold, clean cutting
•Decorative sheet: Stiffness, chemical resistance, forming, even draw
•Food packaging: Not manufactured with BPA, phthalates, or halogens
•Food contact: Broad regulatory approval
 

 

 
Information provided by Dongguan Yiding Plastic Raw Materials Co.,Ltd
Name: Richard Wang
Tel :0086 769 87190386
Mobile:0086 13662834186
Email:Richard_philips@163.com
Skype user: richwang16

Physical Properties Metric English Comments
Oxygen Permeability  970 cm3 mil/(m2 day atm) 62.6 cm3 mil/(100 in2 day atm)  
Water Vapor Permeability  3.70 g mil/ (m2 day) 0.239 g mil/ (100 in2 day)  
Density  1.02 g/cc 0.0368 lb/in³ ISO 1183
Water Absorption at Saturation  0.010 %
@Temperature 23.0 °C
0.010 %
@Temperature 73.4 °F
ISO 62
Thickness  70.0 microns 2.76 mil Film
Melt Flow   1.8 g/10 min
@Load 2.16 kg,
Temperature 190 °C
1.8 g/10 min
@Load 4.76 lb,
Temperature 374 °F
ISO 1133
  10.1 g/10 min
@Load 2.16 kg,
Temperature 230 °C
10.1 g/10 min
@Load 4.76 lb,
Temperature 446 °F
ISO 1133
 
Mechanical Properties Metric English Comments
Film Elongation at Break, MD  3.4 % 3.4 % ISO 527-3
Film Elongation at Break, TD  3.4 % 3.4 % ISO 527-3
Tensile Modulus  1.70 GPa 247 ksi Film, TD; ISO 527-3
  2.10 GPa 305 ksi Film, MD; ISO 527-3
Film Tensile Strength at Break, MD  55.0 MPa 7980 psi ISO 527-3
Film Tensile Strength at Break, TD  50.0 MPa 7250 psi ISO 527-3
 
Thermal Properties Metric English Comments
Glass Transition Temp, Tg  78.0 °C 172 °F 10°C/min; ISO 11357-1,-2,-3
 
Descriptive Properties
Type of film extrusion Cast Test specimen