Topas Advanced Polymers TOPAS® 8007F-04 Cyclic Olefin Copolymer (COC)

Topas Advanced Polymers TOPAS® 8007F-04 Cyclic Olefin Copolymer (COC)

2019-05-28 17:12:11

  

Categories:  Polymer; Thermoplastic; Cyclo Olefin Polymer
 
Material Notes:  TOPAS® 8007F-04 is a general purpose film extrusion grade. It is a high clarity amorphous resin with high stiffness, moisture barrier, chemical resistance, thermoformability and purity for food and healthcare applications. It is used in monolayer cast applications, and in coextrusion in both cast and blown processes, for a wide variety of film and sheet products requiring excellent optics in applications such as blister, twist, barrier, shrink and easy tear packaging. Industrial uses include formed decorative sheet products.
Key applications and attributes:

•Pharmaceutical blisters: Clarity, forming, barrier, purity, halogen-free
•Deep draw barrier trays: Excellent deep draw, unlike other barriers
•Shrink films and labels: High shrink, low stress, gloss, clarity, toughness
•Twist films: High gloss, outstanding deadfold, clean cutting
•Decorative sheet: Gloss, hardness, chemical resistance, forming
•Food packaging: Not manufactured with BPA, phthalates, or halogens
 
 
 

 
Information provided by Dongguan Yiding Plastic Raw Materials Co.,Ltd
Name: Richard Wang
Tel :0086 769 87190386
Mobile:0086 13662834186
Email:Richard_philips@163.com
Skype user: richwang16

 

Physical Properties Metric English Comments
Oxygen Permeability  977 cm3 mil/(m2 day atm) 63.0 cm3 mil/(100 in2 day atm)  
Water Vapor Permeability  3.70 g mil/ (m2 day) 0.239 g mil/ (100 in2 day)  
Density  1.02 g/cc 0.0368 lb/in³ ISO 1183
Water Absorption at Saturation  0.010 %
@Temperature 23.0 °C
0.010 %
@Temperature 73.4 °F
ISO 62
Water Vapor Transmission  0.000800 g/m²/day
@Temperature 38.0 °C
0.0000515 g/100 in²/day
@Temperature 100 °F
90% RH; ISO 15106-3
Thickness  70.0 microns 2.76 mil Film
Melt Flow   1.8 g/10 min
@Load 2.16 kg,
Temperature 190 °C
1.8 g/10 min
@Load 4.76 lb,
Temperature 374 °F
ISO 1133
  11 g/10 min
@Load 2.16 kg,
Temperature 230 °C
11 g/10 min
@Load 4.76 lb,
Temperature 446 °F
ISO 1133
 
Mechanical Properties Metric English Comments
Film Elongation at Break, MD  2.9 % 2.9 % ISO 527-3
Film Elongation at Break, TD  3.0 % 3.0 % ISO 527-3
Tensile Modulus  1.80 GPa 261 ksi Film, TD; ISO 527-3
  2.20 GPa 319 ksi Film, MD; ISO 527-3
Elmendorf Tear Strength MD  225 g 225 g ISO 6383-2
Elmendorf Tear Strength TD  230 g 230 g ISO 6383-2
Dart Drop Test  <= 36.0 g <= 0.0794 lb F50; ISO 7765-1
Film Tensile Strength at Break, MD  57.0 MPa 8270 psi ISO 527-3
Film Tensile Strength at Break, TD  50.0 MPa 7250 psi ISO 527-3
 
Thermal Properties Metric English Comments
Glass Transition Temp, Tg  78.0 °C 172 °F 10°C/min; ISO 11357-1,-2,-3
 
Optical Properties Metric English Comments
Haze  <= 1.0 % <= 1.0 % Film; ISO 14782
Gloss  >= 100 % >= 100 % 60°, Film; ISO 2813
 
Descriptive Properties
Type of film extrusion Cast Test specimen