Topas Advanced Polymers TOPAS® 6017S-04 Cyclic Olefin Copolymer (COC)

Topas Advanced Polymers TOPAS® 6017S-04 Cyclic Olefin Copolymer (COC)

2019-05-28 17:12:04

  

Categories:  Polymer; Thermoplastic; Cyclo Olefin Polymer
 
Material Notes:  TOPAS® 6017S-04 is an injection molding grade with a high heat distortion temperature (170°C) and exceptional dimensional stability. It is a glass-clear amorphous polymer with outstanding moisture barrier, chemical resistance, high purity and a non-reactive surface making it an excellent choice for precision optics, healthcare and other high-tech products. Lower leachables and extractables of TOPAS COC preserve food and drug stability and quality. It is a non-polar substrate that does not promote adsorption, denaturation, aggregation, or precipitation like glass can.
Key applications and attributes:

•Drug delivery: Low leachables & extractables, low water transmission
•Prefilled syringes, vials, cartridges: Non-ionic, does not promote adsorption like glass
•Bottles: Minimally reactive, EtO/gamma/steam sterilizable
•Surgical instruments: Chemically resistant to alcohol, acetone, and acrylates
•IV containers and components: Transparent, withstands EtO/gamma/steam sterilization
•Labware: Temperature resistance, clarity and purity
•Optics: Clarity, low birefringence, low moisture sensitivity
•Electronics: Low dielectric constant, thermoplastic
•Food packaging: Not manufactured with BPA, phthalates, or halogens
•Healthcare and food: Broad regulatory approval 


 
Information provided by Dongguan Yiding Plastic Raw Materials Co.,Ltd
Name: Richard Wang
Tel :0086 769 87190386
Mobile:0086 13662834186
Email:Richard_philips@163.com
Skype user: richwang16

 

Physical Properties Metric English Comments
Density  1.02 g/cc 0.0368 lb/in³ ISO 1183
Water Absorption at Saturation  0.010 %
@Temperature 23.0 °C
0.010 %
@Temperature 73.4 °F
ISO 62
Melt Flow  1.38 g/10 min
@Load 2.16 kg,
Temperature 260 °C
1.38 g/10 min
@Load 4.76 lb,
Temperature 500 °F
ISO 1133
 
Mechanical Properties Metric English Comments
Tensile Strength, Yield  58.0 MPa 8410 psi 5mm/min; ISO 527-2/1A
Elongation at Yield  2.4 % 2.4 % 5mm/min; ISO 527-2/1A
Tensile Modulus  3.00 GPa 435 ksi 1mm/min; ISO 527-2/1A
Charpy Impact Unnotched  1.50 J/cm²
@Temperature 23.0 °C
7.14 ft-lb/in²
@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched  0.160 J/cm²
@Temperature 23.0 °C
0.761 ft-lb/in²
@Temperature 73.4 °F
ISO 179/1eA
 
Electrical Properties Metric English Comments
Volume Resistivity  >= 1.00e+16 ohm-cm >= 1.00e+16 ohm-cm IEC 60093
Dielectric Constant   2.3
@Frequency 1.00e+9 Hz
2.3
@Frequency 1.00e+9 Hz
IEC 60250
  2.35
@Frequency 1000 - 10000 Hz
2.35
@Frequency 1000 - 10000 Hz
IEC 60250
Dissipation Factor  0.0000700
@Frequency 1.00e+9 Hz
0.0000700
@Frequency 1.00e+9 Hz
IEC 60250
Comparative Tracking Index  >= 600 V >= 600 V IEC 60112
 
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi)  170 °C 338 °F ISO 75-1,-2
Vicat Softening Point  178 °C 352 °F B50 (50°C/h 50N); ISO 306
Glass Transition Temp, Tg  178 °C 352 °F 10°C/min; ISO 11357-1,-2,-3
Flammability, UL94  HB
@Thickness 1.60 mm
HB
@Thickness 0.0630 in
 
 
Optical Properties Metric English Comments
Refractive Index  1.53 1.53 ISO 489
Transmission, Visible  91 % 91 % ISO 13468-2
 
Processing Properties Metric English Comments
Feed Temperature  <= 110 °C <= 230 °F  
Nozzle Temperature  260 - 320 °C 500 - 608 °F  
Zone 1  250 - 280 °C 482 - 536 °F  
Zone 2  260 - 300 °C 500 - 572 °F  
Zone 3  270 - 310 °C 518 - 590 °F  
Zone 4  270 - 320 °C 518 - 608 °F  
Mold Temperature  120 - 160 °C 248 - 320 °F  
Injection Velocity  50.0 - 150 mm/sec 1.97 - 5.91 in/sec Moderate to Fast
Injection Pressure  50.0 - 110 MPa 7250 - 16000 psi Specific
Hold Pressure  30.0 - 60.0 MPa 4350 - 8700 psi Specific
Back Pressure  <= 15.0 MPa <= 2180 psi Specific
Screw Speed  50 - 200 rpm 50 - 200 rpm