PA66 79G13HSL

2019-05-28

Physical Properties Metric English Comments
Density  1.21 g/cc 0.0437 lb/in³ DAM; ISO 1183
Water Absorption   2.2 %
@Temperature 23.0 °C 2.2 %
@Temperature 73.4 °F Equilibrium 50%RH; DAM; ISO 62, Similar to
  6.5 %
@Temperature 23.0 °C 6.5 %
@Temperature 73.4 °F Saturation, immersed; DAM; ISO 62, Similar to
Linear Mold Shrinkage, Flow  0.0050 cm/cm
@Thickness 2.00 mm 0.0050 in/in
@Thickness 0.0787 in Parallel; DAM; ISO 294-4
Linear Mold Shrinkage, Transverse  0.0080 cm/cm
@Thickness 2.00 mm 0.0080 in/in
@Thickness 0.0787 in Normal; DAM; ISO 294-4
 
Mechanical Properties Metric English Comments
Hardness, Rockwell M  74 74 50%RH; ISO 2039/2
  90 90 DAM; ISO 2039/2
Tensile Strength at Break   67.0 MPa
@Temperature 23.0 °C 9720 psi
@Temperature 73.4 °F 50%RH; ISO 527
  118 MPa
@Temperature 23.0 °C 17100 psi
@Temperature 73.4 °F DAM; ISO 527
Elongation at Break   4.0 %
@Temperature 23.0 °C 4.0 %
@Temperature 73.4 °F DAM; ISO 527
  10 %
@Temperature 23.0 °C 10 %
@Temperature 73.4 °F 50%RH; ISO 527
Tensile Modulus   3.70 GPa
@Temperature 23.0 °C 537 ksi
@Temperature 73.4 °F 50%RH; ISO 527
  5.10 GPa
@Temperature 23.0 °C 740 ksi
@Temperature 73.4 °F DAM; ISO 527
Izod Impact, Notched (ISO)   4.00 kJ/m²
@Temperature -30.0 °C 1.90 ft-lb/in²
@Temperature -22.0 °F 50%RH; ISO 180/1A
  6.00 kJ/m²
@Temperature -30.0 °C 2.86 ft-lb/in²
@Temperature -22.0 °F DAM; ISO 180/1A
  8.00 kJ/m²
@Temperature 23.0 °C 3.81 ft-lb/in²
@Temperature 73.4 °F DAM; ISO 180/1A
  9.00 kJ/m²
@Temperature 23.0 °C 4.28 ft-lb/in²
@Temperature 73.4 °F 50%RH; ISO 180/1A
Charpy Impact Unnotched   5.40 J/cm²
@Temperature -30.0 °C 25.7 ft-lb/in²
@Temperature -22.0 °F 50%RH; ISO 179/1eU
  5.90 J/cm²
@Temperature -30.0 °C 28.1 ft-lb/in²
@Temperature -22.0 °F DAM; ISO 179/1eU
  5.90 J/cm²
@Temperature 23.0 °C 28.1 ft-lb/in²
@Temperature 73.4 °F 50%RH; ISO 179/1eU
  6.70 J/cm²
@Temperature 23.0 °C 31.9 ft-lb/in²
@Temperature 73.4 °F DAM; ISO 179/1eU
Charpy Impact, Notched   0.600 J/cm²
@Temperature -30.0 °C 2.86 ft-lb/in²
@Temperature -22.0 °F 50%RH; ISO 179/1eA
  0.600 J/cm²
@Temperature -30.0 °C 2.86 ft-lb/in²
@Temperature -22.0 °F DAM; ISO 179/1eA
  0.800 J/cm²
@Temperature 23.0 °C 3.81 ft-lb/in²
@Temperature 73.4 °F DAM; ISO 179/1eA
  1.40 J/cm²
@Temperature 23.0 °C 6.66 ft-lb/in²
@Temperature 73.4 °F 50%RH; ISO 179/1eA
Tensile Creep Modulus, 1 hour  4030 MPa
@Temperature 23.0 °C 585000 psi
@Temperature 73.4 °F 50%RH; ISO 899
Tensile Creep Modulus, 1000 hours  3180 MPa
@Temperature 23.0 °C 461000 psi
@Temperature 73.4 °F 50%RH; ISO 899
 
Electrical Properties Metric English Comments
Comparative Tracking Index  250 V
@Temperature 23.0 °C 250 V
@Temperature 73.4 °F DAM; UL 746A
 
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow  500 µm/m-°C
@Temperature 23.0 - 55.0 °C 278 µin/in-°F
@Temperature 73.4 - 131 °F DAM; ISO 11359-1/-2
CTE, linear, Transverse to Flow  130 µm/m-°C
@Temperature 23.0 - 55.0 °C 72.2 µin/in-°F
@Temperature 73.4 - 131 °F DAM; ISO 11359-1/-2
Deflection Temperature at 0.46 MPa (66 psi)  260 °C 500 °F DAM; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)  242 °C 468 °F DAM; ISO 75-1/-2
UL RTI, Electrical   105 °C
@Thickness 0.810 mm 221 °F
@Thickness 0.0319 in DAM; UL 746B
  120 °C
@Thickness 3.00 mm 248 °F
@Thickness 0.118 in DAM; UL 746B
  120 °C
@Thickness 1.50 mm 248 °F
@Thickness 0.0591 in DAM; UL 746B
UL RTI, Mechanical with Impact   65.0 °C
@Thickness 0.810 mm 149 °F
@Thickness 0.0319 in DAM; UL 746B
  105 °C
@Thickness 3.00 mm 221 °F
@Thickness 0.118 in DAM; UL 746B
  105 °C
@Thickness 1.50 mm 221 °F
@Thickness 0.0591 in DAM; UL 746B
UL RTI, Mechanical without Impact   105 °C
@Thickness 0.810 mm 221 °F
@Thickness 0.0319 in DAM; UL 746B
  120 °C
@Thickness 3.00 mm 248 °F
@Thickness 0.118 in DAM; UL 746B
  120 °C
@Thickness 1.50 mm 248 °F
@Thickness 0.0591 in DAM; UL 746B
Flammability, UL94   HB
@Thickness 3.00 mm HB
@Thickness 0.118 in DAM; IEC 60695-11-10
  HB
@Thickness 1.50 mm HB
@Thickness 0.0591 in DAM; IEC 60695-11-10
  HB
@Thickness 0.810 mm HB
@Thickness 0.0319 in DAM; IEC 60695-11-10
  HB
@Thickness 3.00 mm HB
@Thickness 0.118 in DAM; UL94
  HB
@Thickness 1.50 mm HB
@Thickness 0.0591 in DAM; UL94
  HB
@Thickness 0.810 mm HB
@Thickness 0.0319 in DAM; UL94
 
Processing Properties Metric English Comments
Melt Temperature  263 °C 505 °F 10°C/min; DAM; ISO 11357-1/-3
  295 °C 563 °F DAM; Optimum
  285 - 305 °C 545 - 581 °F DAM
Drying Temperature  80.0 °C 176 °F DAM
Dry Time  2.00 - 4.00 hour 2.00 - 4.00 hour DAM
Moisture Content  <= 0.20 % <= 0.20 % DAM
 
Descriptive Properties
Forms Pellets DAM
Generic Nylon 66 DAM
Material Status Preliminary Data DAM
Part Marking Code >PA66-IGF13< ISO 11469; DAM
Processing Method Injection Molding DAM
Product Category Glass Reinforced Resins DAM
  Toughened Resins DAM
Resin Identification PA66-IGF13 ISO 1043; DAM
RoHS Compliance Contact Manufacturer 
 