Polyamide/PA 6 nylon granule
wear resistance, self-lubrication
oil resistant, resistant to weak acid
free sample
Polyamide/PA 6/ PAP66 nylon granule
PA6-GF30 Reinforcement with 30% Glass fiber;
PA6-GF45 Reinforcement with 45% Glass fiber;
PA6-GF60 Reinforcement with 60% Glass fiber.
|
Properties |
ASTM |
Test Condition |
Unit |
Specifications |
||
|
PA6-GF30 |
PA6-GF45 |
PA6-GF60 |
||||
|
Physical Properties |
||||||
|
Density |
D-792 |
23°C |
g/cm3 |
1.36 |
1.48 |
1.60 |
|
Melt Flow Index |
D-1238 |
260°C/5.0Kg |
g/10min |
15 |
10 |
5 |
|
Water Absorption |
D-570 |
23°C,24hrs |
% |
0.8 |
0.7 |
0.5 |
|
Mold Shrinkage |
D-955 |
23°C |
% |
0.2-0.8 |
0.2-0.6 |
0.2-0.4 |
|
Mechanical Properties |
||||||
|
Tensile Strength |
D-638 |
10mm/min |
MPa |
130 |
170 |
220 |
|
Elongation at Break |
D-638 |
10mm/min |
% |
10 |
8 |
5 |
|
Flexural Strength |
D-790 |
2mm/min |
MPa |
190 |
230 |
320 |
|
Flexural Modulus |
D-790 |
2mm/min |
MPa |
7000 |
10500 |
15000 |
|
IZOD Impact Strength notched |
D-256 |
3.2mm,23°C |
KJ/m2 |
18 |
20 |
21 |
|
Thermal Properties |
||||||
|
H.D.T |
D-648 |
0.45MPa |
°C |
220 |
220 |
220 |
|
Others |
||||||
|
Flammability |
UL-94 |
1.6mm |
— |
HB |
HB |
HB |
|
Glass Fiber Content |
— |
— |
% |
30 |
45 |
60 |
|
Characteristics |
— |
— |
— |
|||
|
Properties |
Test method |
Unit |
Typical values |
|
Tensile strength |
ASTM D-638 |
Mpa |
150 |
|
Elongation at break |
ASTM D-638 |
% |
9 |
|
Flexural strength |
ASTM D-790 |
Mpa |
251 |
|
Bending modulus |
ASTM D-790 |
Mpa |
10707 |
|
Charpy unnotched impact strength |
ASTM D-256 |
KJ/m² |
53 |
|
Lzod notched impact strength |
ASTM D-256 |
KJ/m² |
13 |
|
Ashy |
ASTM D-482 |
% |
55 |